Marpa Lotsawa, full Gold Plated, Antique Finishing, Old Post, Remakable, 24 by 17 cm, made by Copper, Buddhist Statue, Tibetan Masters Guru

Date Added : 2011-11-10 18:00:10 (3305)Views

Marpa Lotsawa, full Gold Plated, Antique Finishing, Old Post, Remakable
Code	HME8316
Size	Height 24cm (9") Width 17cm (7") Depth 12cm (5")
Weight	30000 30 kg - 66.14 lbs
Material	Copper
Availability	Subject to Avilability

Order configuration (Optional)

Filling & Blessing

HIDE

Select Option

Click Here to View All Option and Prices

$43 Filling and Blessing

Select

$37 Filling Only

Select

$14 Blessing Only

Select

Statue Finishing

HIDE

Select Option

Click Here to View All Option and Prices

$45 Partly Gold Plated

Select

$53 Partly Gold Plated with extra gold

Select

$86 HQ, Partly Gold Plated

Select

$45 Electro gold Plated

Select

$58 Electro Gold with painted Face

Select

$58 Electro Gold with Antique finish

Select

$66 Electro Gold Plated with Painted face an

Select

$107 Full Gold with face paint

Select

$98 Full Fire Gold Plated

Select

$147 HQ, Full Fire Gold with face paint

Select

$107 Full Fire Gold Anique Finishing

Select

$151 HQ, Full Fire Gold With Matt Finishing

Select

$160 HQ, Full Fire Gold with Antique Finihsin

Select

$176 HQ Full Gold with Gold Painted Skin

Select

$45 Colors only Basic

Select

$107 Color and Gold Good

Select

$147 Good Quality Color and gold Good Quality

Select

$107 Color Gold and Sivler

Select

$147 HQ, Color and Stond Setting

Select

$209 HQ Gold Empahised Color support

Select

$331 HQ, Cremamic wasable Color, with Gold

Select

$17 Chocolate Oxidized

Select

$17 Dark Chocolate oxidized

Select

$25 Chocolate oxidized with Silver plating

Select

$21 Double Color Oxidation

Select

$21 Chocolate Oxidized with Painted Face

Select

$21 Silver Plated Oxidized

Select

$25 Extra Silver Plated Oxidized with Painte

Select

$29 Silver Plated Double Color Oxidized wit

Select

$53 Silver Plated, Gold ornament, with Doub

Select

$53 Silver Skin and Gold ornaments Plated D

Select

$17 Antique With red Powder

Select

$29 Antique finishing with face paint

Select

$53 Green antique finishing

Select

$78 Painted Antique Finishing

Select

$66 Super Antique

Select

$9 Glossy Finished

Select

$17 Copper Plated

Select

$37 Stone Setting

Select

$41 Stone Setting & Antique Finishing

Select

Quantity

PCS

US$ 700.00

Shipping Cost

5 Seconds

Add To Order Quick Inquiry

Shipping Calculation

weight of 1 Pcs of the product is 30 kg and will cost USD $ 387.65

Select
Item location: kathmandu, Nepal
Worldwide shipping

Dispatch

We normally dispatch the product in 2-5 business days. Else Buyer will be infromed personally about the dispatch Date.

Payment

Paypal | Credit - Debit Card | Bank Transfer | See More

Return

7 days money back, buyer pays return shipping

Welcome to Handmade Handicraft
At Handmade Handicraft, we prioritize simplicity, reflected in our user-friendly website design. We have streamlined the process so everything you need is just a click away.
While our website does not support online shopping, we've incorporated a convenient shopping cart system to assist you in sending us your inquiries. Please note, we do not process payments on our site. All transactions will be handled via email, respecting the inquiries you submit.
Should you encounter any issues while submitting your inquiries, please contact us via mobile app, email, or follow the procedure outlined below. We've provided documentation to guide you through the selection process.

Good selecting Procedure

In every product you will find Order Now and Quick Inquiry buttons, they are the two process of sending us your enquiry.

For Business ordering standard quantity

This website has been designed to incorporate retail and wholesale pricing in one place. You can increase or decrease the quantity based on which you will be provided with suitable prices instantly.

For Business ordering Bluk quantity [Above 100 pcs]

This is not a direct shopping website. So no payments are needed for placing an order. Please feel free to send us an order for the product you are interested in, mentioning the approximate quantity. Based on which we will send you a wholesale price quotation.

Copper full gold plated statue made by loss wax system in patan

Marpa Lotsawa
Marpa Lotsawa (མར་པ་ལོ་ཙཱ་བ་ཆོས་ཀྱི་བློ་གྲོས་, 1012-1097), sometimes known fully as Marpa Chokyi Lodro (Wylie: mar pa chos kyi blo gros) or commonly as Marpa the Translator (Marpa Lōtsawa), was a Tibetan Buddhist teacher credited with the transmission of many Vajrayana teachings from India, including the teachings and lineages of Mahamudra. Due to this the Kagyu lineage, which he founded, is often called Marpa Kagyu in his honour.
Although some accounts relate that the Mahasiddha Naropa was the personal teacher of Marpa, other accounts suggest that Marpa held Naropa's lineage through intermediary disciples only. Either way, Marpa was a personal student of the Mahasiddha Maitripa and of the dakini Niguma. Read More

life Story
Born as Marpa Chokyi Lodro, in Lhodrak Chukhyer in the southern part of Tibet, to an affluent family, he began studying at a young age but was wild and untamed compared to other children. Marpa first received instruction for three years at Mangkhar with Drokmi Shakya Yeshe and mastered Sanskrit. He decided to travel to India to study with renowned Indian Buddhist masters. His first trip to Nepal and India was in the company of Nyo Lōtsawa, whom he attended as a servant. Marpa returned home to Lhodrak and converted his entire inheritance into gold to fund his travel expenses and to make offerings to teachers.

Marpa journeyed first to Nepal where he studied with Paindapa and Chitherpa, two famous students of Naropa. Paindapa later accompanied Marpa to Pullahari, near Nalanda University, where Naropa taught. Marpa spent twelve years studying with Naropa and other great Indian gurus, most prominently Maitripada. After twelve years he set forth on his journey back to Tibet to teach and continue his dharma activities.

Marpa was to travel to India twice more and Nepal three more times and studied with Naropa and other great teachers including Maitripa. He is said to have stayed in the cave at Phugtal Monastery. On his third visit to India, Naropa, who was engaged in tantric practices, proved difficult to find. However eventually Marpa found him and received the final teachings and instructions from Naropa. It was then that Naropa prophesied that a family lineage would not continue for Marpa, but that his lineage would be carried on by his disciples. Marpa now had received the full transmission, so Naropa formally declared Marpa to be his successor although he had other major disciples including Paindapa, Chitherpa, Shri Shantibhadra or Kukuripa, and Maitripa.

Upon his return to Tibet, Marpa spent many years translating Buddhist scriptures and made a major contribution to the transmission of the complete buddhadharma to Tibet. Marpa continued to practice and give teachings and transmissions to many students in Tibet. After his second visit to India Milarepa became his disciple. After the death of Marpa's son, Darma Dode, Milarepa inherited his lineage in full. Marpa lived with his wife Dakmema and their sons in Lhodrak in the southern part of Tibet. Marpa is said to have founded Stongdey Monastery in Zanskar in 1052 CE.


A traditional depiction of Marpa painted on a rock on Holy Isle, Firth of Clyde	Lotsawa Marpa Chokyi Lodro, (1012-1097)

OLD POST
Please note that this Marpa Lotsawa is an old post. We typically do not remove our posts from the website for various reasons, such as nostalgia and maintaining page ratings. These posts are not intended for direct sales, but occasionally, we can remake the items.

Remakable
Please note that the Marpa Lotsawa we posted some time ago is not currently available in our store. However, due to the possibility of a remake, it is still on sale. The remake will not be an exact replica of the original statue shown in the picture and will require additional time to be ready for dispatch. If you are willing to wait for this custom remake, you may proceed with your order. Thank you for your understanding and patience.

Full Gold Gilded with Antique Patina.
The Marpa Lotsawa has full gold plated antique finishing. This finishing is a combination of fire mercury gold plating and antique finishing. This traditional technique involves the application of a genuine layer of gold onto the Marpa Lotsawa using the time-honored process of mercury gold plating. Skilled artisans meticulously handle the amalgamation of gold with mercury, ensuring precise application and a truly authentic result. To enhance its charm further, the Marpa Lotsawa undergoes an antique finishing process. This meticulous treatment adds a touch of age and character to the gold plating, creating a sense of antiquity. Through careful craftsmanship and the application of specialized techniques, the Marpa Lotsawa acquires a beautifully aged appearance that adds depth and uniqueness to its overall aesthetic.

The fire mercury gold plating with antique finishing showcases the artisan's dedication to preserving traditional techniques and capturing the essence of timeless elegance. The combination of gold plating and antique finishing lends the Marpa Lotsawa an exquisite and enchanting allure, making it a cherished piece that stands out with its enduring beauty.

Detailed Description of Mercury Gilding - Source wikipedia
Fire-gilding or Wash-gilding is a process by which an amalgam of gold is applied to metallic surfaces, the mercury being subsequently volatilized, leaving a film of gold or an amalgam containing 13 to 16% mercury. In the preparation of the amalgam, the gold must first be reduced to thin plates or grains, which are heated red-hot, and thrown into previously heated mercury, until it begins to smoke. When the mixture is stirred with an iron rod, the gold is totally absorbed. The proportion of mercury to gold is generally six or eight to one. When the amalgam is cold, it is squeezed through chamois leather to separate the superfluous mercury; the gold, with about twice its weight of mercury, remains behind, forming a yellowish silvery mass with the consistency of butter.

When the metal to be gilded is wrought or chased, it ought to be covered with mercury before the amalgam is applied, that this may be more easily spread; but when the surface of the metal is plain, the amalgam may be applied to it directly. When no such preparation is applied, the surface to be gilded is simply bitten and cleaned with nitric acid. A deposit of mercury is obtained on a metallic surface by means of quicksilver water, a solution of mercury(II) nitrate, the nitric acid attacking the metal to which it is applied, and thus leaving a film of free metallic mercury.

The amalgam being equally spread over the prepared surface of the metal, the mercury is then sublimed by a heat just sufficient for that purpose; for, if it is too great, part of the gold may be driven off, or it may run together and leave some of the surface of the metal bare. When the mercury has evaporated, which is known by the surface having entirely become of a dull yellow color, the metal must undergo other operations, by which the fine gold color is given to it. First, the gilded surface is rubbed with a scratch brush of brass wire, until its surface is smooth.

It is then covered with gilding wax, and again exposed to fire until the wax is burnt off. Gilding wax is composed of beeswax mixed with some of the following substances: red ochre, verdigris, copper scales, alum, vitriol, and borax. By this operation the color of the gilding is heightened, and the effect seems to be produced by a perfect dissipation of some mercury remaining after the former operation. The gilt surface is then covered over with potassium nitrate, alum or other salts, ground together, and mixed into a paste with water or weak ammonia. The piece of metal thus covered is exposed to heat, and then quenched in water.

By this method, its color is further improved and brought nearer to that of gold, probably by removing any particles of copper that may have been on the gilt surface. This process, when skillfully carried out, produces gilding of great solidity and beauty, but owing to the exposure of the workmen to mercurial fumes, it is very unhealthy. There is also much loss of mercury to the atmosphere, which brings extremely serious environmental concerns as well.

This method of gilding metallic objects was formerly widespread, but fell into disuse as the dangers of mercury toxicity became known. Since fire-gilding requires that the mercury be volatilized to drive off the mercury and leave the gold behind on the surface, it is extremely dangerous. Breathing the fumes generated by this process can quickly result in serious health problems, such as neurological damage and endocrine disorders, since inhalation is a very efficient route for mercuric compounds to enter the body. This process has generally been supplanted by the electroplating of gold over a nickel substrate, which is more economical and less dangerous.

Fire Gold Plating In Nepal

Lost-Wax System
This Marpa Lotsawa is made by the process of the Lost-Wax system. The lost-wax process, also known as investment casting, is a time-honored technique used to create metal sculptures. It involves several steps that have been practiced for thousands of years. Skilled artisans begin by sculpting a detailed wax model, capturing every intricate detail of the desired sculpture. The wax model is then coated with a ceramic shell, formed by multiple layers of ceramic material. Once the shell has cured, the wax is melted and drained out, leaving behind a cavity. Molten metal is poured into the cavity, creating a precise replica of the original wax model. After the metal has cooled and solidified, the ceramic shell is carefully removed, revealing the final metal sculpture.

Process of loss wax system
The lost-wax process offers exceptional quality control and customization, making it a preferred choice for artists seeking intricate and personalized metal artwork. Despite the availability of newer methods, the traditional lost-wax technique continues to be valued for its historical significance and the craftsmanship it embodies.

The method of metal casting in which molten metal is poured into a mold that has been created by means of a wax model. Once the mold is made, the wax model is melted and drained away. Bronze statues come to life differently than marble statues. Instead of carving a block or marble, the bronze artist uses the lost-wax technique to make a series of molds and then pours melted bronze into the final mold to create the sculpture. This method has been around since 4500 BCE.

There are a few important steps in the lost wax casting process:
Step 1: Sculpting ( It all starts in the studio with an idea, Then figuring out how to realize the vision in clay.)
Step 2: Mold Making.
Step 3: Wax Pouring.
Step 5: Wax Spring.
Step 6: Shell Dipping.
Step 7: Bronze Pouring.

Interestingly enough Loss wax process is also called Investment casting because after layers have been formed and dried, the wax is melted out of the ceramic tree by using steam (120°C) in an autoclave. This is why it is called "lost wax casting". The majority of the molten wax can then be regenerated and reusable.

Before Making statue :At work room making the wax models.	Softening a piece of wax over a brazier.	Relaxing after softening the wax The working environment with works in progress.
Working the face of an Ekajata wax model.	Working the face of wax model.Using a modeling tool to form the face of Ekajata.	Deatail of wax model
The design for Ekajata compared to the Tibetan book on which it was based.Statues Maker Are master in buddhism .	Detail of A partially finished Candamaharoshana (Acala) wax figure made in the Tibetan style.	A finished wax image of Mahakala.
Anthor Finished Wax Model of Shakyamuni Buddha	One of the modelers working in the room shows the Pehar image on which he is working.	The artist showed how the goat , which had been completed earlier, fits under the image. ,
Tej Jyoti Shakya and his wife, Nani Maya Shakya Covering the wax model in a mixture of clay and dung	Pressing the mixture of clay and dung around the wax image.	The board with the clay and dung mixture ready for use.
Model Pieces drying after the initial (dipped) thin layer of fine clay.	Clay-covered model pieces drying in the sun.	Molds waiting to be put into the burnout furnace
The same molds, seen in the previous image, in the burnout furnace	The double row of refractory bricks used to support the heated molds during casting.	The melting furnace and a pile of coke used for melting the metals. Laying the bed of coke in the melting furnace.
The first ignition of the coke.	Checking the coke bed.	The electric blower used to force air into the melting furnace
Beginning to fill the crucibles with scrap copper.	Preparing the bed of burning coke to receive the crucibles	Sorting various metals used in the alloys.
Weighing precious metals that are used in the alloys	Weighing copper from Singapore to achieve a correct alloy.	Different sizes of crucibles and various types of metals to be cast in this melt.
Placing the crucibles in the bed of coke filled with metal are in place.	After the crucibles are in place, more coke is piled around them.	The crucibles are covered with scrap metal to hold in the heat.
The electric fan is then connected.Soon a very hot flame is produced.	The entire furnace temperature goes up to about 1800 -1900 degrees.	Setting up molds in between the refractory bricks to receive the molten metal. Handling the molds with asbestos gloves and bracing them with fragments of bricks.
Pouring the molten metal into the base of a mold	Another view of the artists pouring the molten metal.Detailed view showing the molten metal being poured into the sprues.	Preparing to lift and pour molten metal from one of the larger crucibles.
Cooling a mold containing the recently poured metal.	Beginning to break away the clay mold from the metal casting. The mold breaks away revealing the metal image inside	The first metal image from the day's work.
Examining the image for flaws	Two auras (prabhamandalas), one that cast perfectly and one (in front) that only partially filled.	Opening more molds

Researchers mark specific metal images for future identification.	Cleaning the details of the image with a metal tool.	Sawing off the sprues from Aura image. The sprue metal will be reused in future castings.

Two auras that worked perfectly. The one on the right has been cut off of the sprues, while the one on the left still has the sprues attached.	The finishing specialist begins the finishing process with a set of tools, including a small hammer. to give more detail	The entire surface of the image will be gently hammered to a final, almost polished finish.

The finisher's tools and the work in progress	Finishing work on an image of the Buddha.	Hammering the chest of an image that is being held against the work block

A Buddha image hammered and chased to the final, detailed finish.	Cleaning in a very mild acid bath. The image and prabhamandala are placed in a final acidic bath to make sure the surface is absolutely clean.	Drying the image with a blow torch.